Polyamide 12 30% Glass Filled Plastic Material Properties.Datasheet for Polyamide 12 30% Glass Filled Material Properties.
Thermoplastic
Good rigidity, tensile strength, creep resistance, heat distortion temperature and impact properties. Low mould shrinkage and good dimensional stability compared with unmodified PA 12.
Brittle, low elongation at break and low impact strength compared with unmodified PA 12. Mechanical properties of moulding can be highly anisotropic.
Electric plugs, clock parts, watchcases, ski boot clasps, fixture and fittings, fan blades, heat resistant machine housings, gear wheels, needle mounts for injection and blood transfusion equipment, high precision parts. Watchcases, switches, slide gauges, and instrument casings.
Property |
Value |
Density (g/cm3) |
1.25 |
Surface Hardness |
RR113 |
Tensile Strength (MPa) |
80 |
Flexural Modulus (GPa) |
4 |
Notched Izod (kJ/m) |
0.1 |
Linear Expansion (/°C x 10-5) |
5 |
Elongation at Break (%) |
7 |
Strain at Yield (%) |
N/A |
Max. Operating Temp. (°C) |
70 |
Water Absorption (%) |
0.15 |
Oxygen Index (%) |
21 |
Flammability UL94 |
V2 |
Volume Resistivity (log ohm.cm) |
15 |
Dielectric Strength (MV/m) |
45 |
Dissipation Factor 1kHz |
0.04 |
Dielectric Constant 1kHz |
4.5 |
HDT @ 0.45 MPa (°C) |
170 |
HDT @ 1.80 MPa (°C) |
160 |
Material. Drying hrs @ (°C) |
2 @ 90 |
Melting Temp. Range (°C) |
200 - 240 |
Mould Shrinkage (%) |
0.5 |
Mould Temp. Range (°C) |
40 - 80 |