EVA Polymer Material Properties and Technical InformationSearch for eva ethylene vinyl acetate datasheet, ethylene vinyl acetate, plastic material datasheets and plastic materials information on Plastixportal.
Thermoplastic
Lower water absorption and cost, higher tensile strength, permeability, modulus and dielectric strength than EVA with 25% or 33% VA.
Lower heat seal strength, flexibility and low temperature performance compared with EVA containing 25% or 33% VA.
Property |
Value |
Density (g/cm3) |
0.935 |
Surface Hardness |
SA95 |
Tensile Strength (MPa) |
19 |
Flexural Modulus (GPa) |
0.07 |
Notched Izod (kJ/m) |
1.06+ |
Linear Expansion (/°C x 10-5) |
18 |
Elongation at Break (%) |
750 |
Strain at Yield (%) |
N/A |
Max. Operating Temp. (°C) |
50 |
Water Absorption (%) |
0.05 |
Oxygen Index (%) |
19 |
Flammability UL94 |
HB |
Volume Resistivity (log ohm.cm) |
16 |
Dielectric Strength (MV/m) |
30 |
Dissipation Factor 1kHz |
0.015 |
Dielectric Constant 1kHz |
2.65 |
HDT @ 0.45 MPa (°C) |
20- |
HDT @ 1.80 MPa (°C) |
20- |
Material. Drying hrs @ (°C) |
NA |
Melting Temp. Range (°C) |
160 - 220 |
Mould Shrinkage (%) |
2 |
Mould Temp. Range (°C) |
20 - 40 |
NOTE: The information contained herein are typical values intended for reference and comparison purposes only. They should NOT be used as a basis for design specifications or quality control. All values at 73°F (23°C) unless otherwise noted.